Golden-A

Cream colored, finely ground rubbery form

Characteristic Application

Completely non extractable, non volatile, non staining, non swelling grade of factice.

Compatible with NBR, PVC-NBR, NEOPRENE, BUTYL, HYPALON, SBR, NR etc.

Suggested Uses

Printing rollers, Textile cots and apron, oil seals, soft colored natural rubber products, cork sheets, tennis balls, shoe soles, rubber mats, Hydraulic hoses, LPG hoses, all nitrile and PVC-Nitrile molded products, light colored bicycle tires etc.

Noswell

Light brown-maroon in granular form

Characteristics Application

Non swelling, non extractable, non volatile grade of factice, Compatible with all synthetic polymers.

Suggested Uses

Petroleum hoses, Hydraulic hoses, Automobile parts, oil seals etc.

Softex

Soft brown lumps

Characteristics Application

Partly extractable, Compatible with NR, SBR, NBR, PVC-NBR, NEOPRENE, EPDM. Can partly replace expensive plasticizers like DOP.

Gives very good scorch safety in NEOPRENE and effectively controls blooming in EPDM.

Suggested Uses

Bicycle tubes, Auto tubes, Natural rubber hoses, Water hoses, Neoprene hoses, EPDM profiles, Automobile door seals, In printing rollers for low shore hardness, sponge rubber etc.

BS

Brown lumps

Characteristics Application

Partly extractable. Extensively used in thick articles for better and uniform curing. Imparts medium shore hardness. Improves scorch safety. Compatible with all grades of synthetic and natural polymers.

Suggested Uses

Railway pads, Rubber vibration insulator, Automobile parts, bellows, Thick articles of all polymers etc.

Uniplast :

Series of process oils. Successfully and comfortably replaces DOP, DOA, RPO etc from rubber compounding.
REACH Compliant product range.
Economical than DOP.
Imparts Excellent Properties without additional cost.

Actual Color of Oil

Uniplast Oil-A      a REACH Compliant Product

Properties

Uniplast Oil-A is recommended for Nitrile , Pvc- Nitrile and Natural Rubber for dark coloured goods.

Can replace 100% DOP, DOA, RPO etc plasticizers from NBR, PVC-NBR and Natural Rubber.

Characteristic Applications

Non Extractable, Non Migrating, Non Volatile Oil Thus Improves After Aging Properties.

Imparts Very High Flex Properties.

Improves Tear Strength.

Imparts Good Building Tack in NBR and PVC-NBR rubbers Compounds.

Improves Metal to Rubber and Cord to Rubber Bonding.

Imparts Low Temperature Flexibility up to – 40° C

Actual Color of Oil

Uniplast Oil-B      a REACH Compliant Product

Properties

Uniplast Oil-B is recommended for Neoprene (CR) and Natural Rubber, even for light coloured goods.

Can replace 100% DOP,RPO etc plasticizers from Neoprene and Natural Rubber.

Characteristic Applications

Imparts Cure Safety in Neoprene Rubber (CR) by reducing frictional heat generated during the process of Compounding , Extrusion and Injection Molding.

Imparts Good Building Tack in Neoprene rubber compound.

Non Extractable, Non Migrating, Non Volatile Oil Thus Improves After Aging Properties.

Imparts High Flex Properties.

Improves Tear Strength and Abrasion Resistance.

Improves Metal to Rubber and Cord to Rubber Bonding.

Imparts Low Temperature Flexibility up to – 40° C

Actual Color of Oil

Uniplast Oil-C         a REACH Compliant Product

Properties

Uniplast Oil-C is recommended for Nitrile , Pvc- Nitrile and Natural Rubber, even for light colored goods.

Can replace 100% DOP, DOA, RPO etc plasticizers from NBR, PVC-NBR and Natural Rubber.

Characteristic Applications

Non Staining.

Non Extractable, Non Migrating, Non Volatile Oil Thus Improves After Aging Properties.

Improves Mold Flow Propeties of the compound.

Imparts Higher Flex Properties.

Improves Tear Strength.

Supports Good Building Tack in NBR and PVC-NBR rubbers.

Supports Metal to Rubber and Cord to Rubber Bonding.

Imparts Low Temperature Flexibility up to – 40° C

Actual Color of Oil

Unipol      a REACH Compliant Product

Properties:

Unipol comes in a bale form.

Unipol is a long chain agro base polymer.

Unipol is Compatible with Nitrile, PVC-Nitrile, Natural Rubber.

Can be blended in 5 to 30 phr proportion depending upon the final properties required.

Reduces cost of compound.

Characteristic Applications:

During Compounding and Before Curing:

Imparts Good Building Tack to the Compound.

Improves Mold flow.

Improves Self Adhesion , hence advisable for Rubber to Cord Adhesion Applications.

Enhances Filler Loading Capacity of the compound.

After Curing:

Non Extractable, Non Migrating additive, Thus Improves After Aging Properties.

Gives shiner surface finish to the final product.